Cupping of resawn lumber
The two reasons wood cups when resawn. 1998.
by Professor Gene Wengert
I've recently experienced cupping problems when I've resawn lumber. Is there anything I can do to reduce (or eliminate) the cupping?
There are two reasons for cupping of resawn lumber. First, if the cupping occurs when resawing (or if any warp occurs while machining) and there are no severe moisture gradients from shell to core, the cause is drying stress (also called "casehardening," although the case is not harder than the core). Drying stresses are normal--they result because the outside wood fibers begin to shrink very early in drying, but are restrained by the core, which isn't yet ready to shrink. Thus, the outer fibers are left in a "stretched out" condition, which is called casehardening, when drying is completed. The second cause, characterized by the warp showing up an hour, week, or month after resawing, is moisture content differences between shell and core.
Many try to reverse the damage done to hardwood lumber by drying stress through "conditioning," a simple steaming treatment performed after drying. In the conditioning process, moisture is quickly added to the outer fibers, which try to swell but cannot because the core... This is the reverse of what caused the stress originally. Now the opposite stress has developed, which offsets the casehardening stress. Conditioning is so fast and easy, it is hard to imagine why anyone would not deliver lumber that is free of transverse (across the grain) drying stress.
Hopefully, you didn't pay much (or anything) for this improperly dried lumber.
It's interesting to note that resawning can introduce stresses along the length (longitudinal) of the board that cause the piece to bow or side bend when ripping. These stresses are more difficult to remove.
It is axiomatic in the wood drying business, however, that the best dried wood is wood that you dry yourself. Another rule is to resaw green, if at all possible, and dry the thinner material.
Professor Gene Wengert is Extension Specialist in Wood Processing at the Department of Forestry, University of Wisconsin-Madison.
Click on Wood Doctor Archives to peruse past answers.
If you would like to obtain a copy of "The Wood Doctor's Rx", visit the Wood Education and Resource Center Web site for more information.
Would you like to add information to this article?
Interested in writing or submitting an article?
Have a question about this article?
Have you reviewed the related Knowledge Base areas below?
KnowledgeBase: Lumber & Plywood: Storage
KnowledgeBase: Primary Processing: Kiln Operation
KnowledgeBase: Solid Wood Machining: General
KnowledgeBase: Wood Engineering: Wood Properties
KnowledgeBase: Knowledge Base
All rights reserved. No part of this publication may be reproduced in
any manner without permission of the Editor.
Review Woodweb.com's Copyright Policy.
The editors, writers, and staff at Woodweb.com try to promote safe practices.
What is safe for one woodworker under certain conditions may not be safe
for others in different circumstances. Readers should undertake the use
of materials and methods discussed at Woodweb.com after considerate evaluation,
and at their own risk.
865 Troxel Road
Lansdale, PA 19446
Copyright © 1996-2021 - Woodweb.com